POLYMER SEARCH

Old Hickory 54-S Kentucky Ball Clay

Category	Ceramic , Clay , Ball Clay
Manufacturer	Old Hickory Clay Co.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Old Hickory 54-S Kentucky Ball Clay.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This ball clay is a multi- purpose clay that has excellent pressing, extrusion, and casting qualities. It has a moderately fine particle size distribution and the high plasticity and dry strength is due in part to unique mineralogy of the clay. The low total carbon content provides excellent oxidation characteristics to a variety of ceramic process formulas.Information provided by Old Hickory Clay Company

Physical Properties	Metric	English	Comments
Particle Size	0.50 µm	0.50 µm	48% of particles less than
	0.63 µm	0.63 µm	Median particle diameter
	1.0 µm	1.0 µm	60% of particles less than
	<= 5.0 µm	<= 5.0 µm	84% of particles less than
pH	5.8	5.8
Soluble Sulfates	400 ppm	400 ppm
Specific Surface Area	22.4 m²/g	22.4 m²/g

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00434 GPa	0.630 ksi	Dry Modulus of Rupture for 50% clay/50% flint, cast bars

Thermal Properties	Metric	English	Comments
Shrinkage	5.1 %	5.1 %	Cone 04, Linear Fired Shrinkage
	6.0 %	6.0 %	Cone 3, Linear Fired Shrinkage
	6.5 %	6.5 %	Linear Drying Shrinkage
	7.2 %	7.2 %	Cone 11, Linear Fired Shrinkage

Component Elements Properties	Metric	English
Al2O3	28.44 %	28.44 %
CaO	0.16 %	0.16 %
Fe2O3	1.28 %	1.28 %
K2O	0.89 %	0.89 %
Loss on Ignition(%)	9.62 %	9.62 %
MgO	0.42 %	0.42 %
Na2O	0.090 %	0.090 %
SiO2	57.09 %	57.09 %
TiO2	1.93 %	1.93 %

Descriptive Properties	Value	Comments
Absorption (%)	12.1	Cone 04, Fired
	4.4	Cone 11, Fired
	9.6	Cone 3, Fired
CEC/MBI (meg/100 ml)	8.9
Crude Color	Light Grey
Filtration (ml)	21
Pyrometric Cone Equivalent (PCE)	31-32
Water of Plasticity (%)	32
Wet Sieve Residue (%)	0.92	Wet Sieve Residue, +200 mesh