Haynes HR-160® alloy, solution annealed sheet

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes HR-160® alloy, solution annealed sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming and welding characteristics. Applications include a variety of fabricated components in municipal, industrial, hazardous, and nuclear waste heat recovery systems. Also suitable for utility boilers, sulfur plants, high-temperature furnaces, kilns, calciners, resource recovery units, cement kilns, pulp and paper recovery boilers, coal gasification systems, and fluidized-bed-combustion systems.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.08 g/cc
0.292 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 758 MPa
110000 psi
33.0 MPa

@Temperature 1204 °C
 4790 psi

@Temperature 2199 °F
46.0 MPa

@Temperature 1149 °C
 6670 psi

@Temperature 2100 °F
68.0 MPa

@Temperature 1093 °C
 9860 psi

@Temperature 1999 °F
129 MPa

@Temperature 982 °C
 18700 psi

@Temperature 1800 °F
241 MPa

@Temperature 871 °C
 35000 psi

@Temperature 1600 °F
421 MPa

@Temperature 760 °C
 61100 psi

@Temperature 1400 °F
519 MPa

@Temperature 649 °C
 75300 psi

@Temperature 1200 °F
569 MPa

@Temperature 538 °C
 82500 psi

@Temperature 1000 °F
Tensile Strength, Yield 353 MPa

@Strain 0.200 %
 51200 psi

@Strain 0.200 %
14.0 MPa

@Strain 0.200 %,
Temperature 1204 °C
 2030 psi

@Strain 0.200 %,
Temperature 2199 °F
19.0 MPa

@Strain 0.200 %,
Temperature 1149 °C
 2760 psi

@Strain 0.200 %,
Temperature 2100 °F
32.0 MPa

@Strain 0.200 %,
Temperature 1093 °C
 4640 psi

@Strain 0.200 %,
Temperature 1999 °F
66.0 MPa

@Strain 0.200 %,
Temperature 982 °C
 9570 psi

@Strain 0.200 %,
Temperature 1800 °F
110 MPa

@Strain 0.200 %,
Temperature 871 °C
 16000 psi

@Strain 0.200 %,
Temperature 1600 °F
212 MPa

@Strain 0.200 %,
Temperature 760 °C
 30700 psi

@Strain 0.200 %,
Temperature 1400 °F
215 MPa

@Strain 0.200 %,
Temperature 649 °C
 31200 psi

@Strain 0.200 %,
Temperature 1200 °F
225 MPa

@Strain 0.200 %,
Temperature 538 °C
 32600 psi

@Strain 0.200 %,
Temperature 1000 °F
Elongation at Break 63 %
63 %
in 50.8 mm
41 %

@Temperature 871 °C
 41 %

@Temperature 1600 °F
 in 50.8 mm
47 %

@Temperature 760 °C
 47 %

@Temperature 1400 °F
 in 50.8 mm
51 %

@Temperature 982 °C
 51 %

@Temperature 1800 °F
 in 50.8 mm
53 %

@Temperature 1093 °C
 53 %

@Temperature 1999 °F
 in 50.8 mm
62 %

@Temperature 649 °C
 62 %

@Temperature 1200 °F
 in 50.8 mm
73 %

@Temperature 538 °C
 73 %

@Temperature 1000 °F
 in 50.8 mm
91 %

@Temperature 1204 °C
 91 %

@Temperature 2199 °F
 in 50.8 mm
107 %

@Temperature 1149 °C
 107 %

@Temperature 2100 °F
 in 50.8 mm
Modulus of Elasticity 211 GPa
30600 ksi
RT
137 GPa

@Temperature 980 °C
 19900 ksi

@Temperature 1800 °F
145 GPa

@Temperature 925 °C
 21000 ksi

@Temperature 1700 °F
150 GPa

@Temperature 870 °C
 21800 ksi

@Temperature 1600 °F
154 GPa

@Temperature 815 °C
 22300 ksi

@Temperature 1500 °F
158 GPa

@Temperature 760 °C
 22900 ksi

@Temperature 1400 °F
163 GPa

@Temperature 705 °C
 23600 ksi

@Temperature 1300 °F
168 GPa

@Temperature 650 °C
 24400 ksi

@Temperature 1200 °F
173 GPa

@Temperature 595 °C
 25100 ksi

@Temperature 1100 °F
177 GPa

@Temperature 540 °C
 25700 ksi

@Temperature 1000 °F
180 GPa

@Temperature 480 °C
 26100 ksi

@Temperature 896 °F
183 GPa

@Temperature 425 °C
 26500 ksi

@Temperature 797 °F
187 GPa

@Temperature 370 °C
 27100 ksi

@Temperature 698 °F
192 GPa

@Temperature 315 °C
 27800 ksi

@Temperature 599 °F
197 GPa

@Temperature 260 °C
 28600 ksi

@Temperature 500 °F
201 GPa

@Temperature 205 °C
 29200 ksi

@Temperature 401 °F
204 GPa

@Temperature 150 °C
 29600 ksi

@Temperature 302 °F
208 GPa

@Temperature 90.0 °C
 30200 ksi

@Temperature 194 °F
210 GPa

@Temperature 40.0 °C
 30500 ksi

@Temperature 104 °F
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Temperature 25.0 - 95.0 °C
 7.22 µin/in-°F

@Temperature 77.0 - 203 °F
13.7 µm/m-°C

@Temperature 25.0 - 205 °C
 7.61 µin/in-°F

@Temperature 77.0 - 401 °F
14.0 µm/m-°C

@Temperature 25.0 - 315 °C
 7.78 µin/in-°F

@Temperature 77.0 - 599 °F
14.4 µm/m-°C

@Temperature 25.0 - 425 °C
 8.00 µin/in-°F

@Temperature 77.0 - 797 °F
14.9 µm/m-°C

@Temperature 25.0 - 540 °C
 8.28 µin/in-°F

@Temperature 77.0 - 1000 °F
15.5 µm/m-°C

@Temperature 25.0 - 600 °C
 8.61 µin/in-°F

@Temperature 77.0 - 1110 °F
15.7 µm/m-°C

@Temperature 25.0 - 700 °C
 8.72 µin/in-°F

@Temperature 77.0 - 1290 °F
16.6 µm/m-°C

@Temperature 25.0 - 800 °C
 9.22 µin/in-°F

@Temperature 77.0 - 1470 °F
17.1 µm/m-°C

@Temperature 25.0 - 900 °C
 9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Specific Heat Capacity 0.462 J/g-°C
0.110 BTU/lb-°F
RT
0.653 J/g-°C

@Temperature 700 °C
 0.156 BTU/lb-°F

@Temperature 1290 °F
0.672 J/g-°C

@Temperature 800 °C
 0.161 BTU/lb-°F

@Temperature 1470 °F
0.689 J/g-°C

@Temperature 900 °C
 0.165 BTU/lb-°F

@Temperature 1650 °F
0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001112 ohm-cm
0.0001112 ohm-cm
RT
0.0001231 ohm-cm

@Temperature 700 °C
 0.0001231 ohm-cm

@Temperature 1290 °F
0.0001238 ohm-cm

@Temperature 800 °C
 0.0001238 ohm-cm

@Temperature 1470 °F
0.0001245 ohm-cm

@Temperature 900 °C
 0.0001245 ohm-cm

@Temperature 1650 °F
0.0001252 ohm-cm

@Temperature 1000 °C
 0.0001252 ohm-cm

@Temperature 1830 °F
0.0001259 ohm-cm

@Temperature 1100 °C
 0.0001259 ohm-cm

@Temperature 2010 °F
0.0001267 ohm-cm

@Temperature 1200 °C
 0.0001267 ohm-cm

@Temperature 2190 °F