SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D 792 |
| 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.013 - 0.015 cm/cm @Time 86400 sec |
0.013 - 0.015 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
| 75.0 MPa | 10900 psi | ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D 638 |
| 2.8 % | 2.8 % | ISO 527 | |
| Tensile Modulus | 4.06 GPa | 589 ksi | 1 mm/min; ISO 527 |
| 6.20 GPa | 899 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
| 111 MPa | 16100 psi | ISO 178 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | ASTM D 790 |
| 3.60 GPa | 522 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.77 J/cm @Temperature 23.0 °C |
5.19 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 87.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 57.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 188 °C @Thickness 3.20 mm |
370 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Kolon SPESIN® KP211 General Purpose PBT Resin
- LG Chemical LUTENE FB0800 LDPE Blown Film
- Solvay TECHNYL® B 230 PA66/6, DRY
- Solvay Specialty Polymers Algoflon® F 5/S Polytetrafluoroethylene (PTFE)
- Wingate Alloys Winco CBS Steel Chockblocks, Buttons, Skidblocks
- Zeon Chemicals Nipol® DN4050 Nitrile Elastomer
- Chosun Refractories SF-S Hard Fireclay brick
- Bapolene® 4082NA Polypropylene
- 3M Scotch-Weld™ PR600 Plastic and Rubber Instant Adhesive
- Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved