Eurostar Staramide RF007S PA66, 35% Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RF007S PA66, 35% Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RF007S is a 35% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Flexural Yield Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Plansee MoCu30 Molybdenum-Copper
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced
- SABIC Innovative Plastics Lexan® 241R PC (Europe-Africa-Middle East)
- Radici Heraflex® A 55 42 I HW2E TPS-SEBS Thermoplastic Elastomer
- Minelco Reclaimed Mid Alumina
- Crucible Steel 174 SXR Precipitation Hardening Stainless Steel
- DuPont Performance Polymers Hytrel® HTR8636 NC010 TPC-ET (Unverified Data**)
- Braskem GD5160 HDPE Blow Molding Polyethylene Homopolymer
- A. Schulman POLYFORT™ PP 3726
- DuPont Bynel® 41E712 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved