Eurostar Staramide PF004EUC PA6, 20% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PF004EUC PA6, 20% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PF004EUC is a 20% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0034 cm/cm @Thickness 4.00 mm |
0.0034 in/in @Thickness 0.157 in |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 7.6 % | 7.6 % | Flexural, 2 mm/min; ISO 178 | |
| Tensile Modulus | 0.0630 GPa | 9.14 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 147 MPa | 21300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 163 MPa | 23600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Zone 1 |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Zone 2 |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Zone 3 |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Honeywell ACLAR® 22C (5.00 mil) Copolymer Film (discontinued **)
- SABIC Innovative Plastics Ultem ATX100F PEI+PCE
- Sumitomo Bakelite North America E 3812M-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy
- Plenco 4349 Phenolic, Granular, Compression Molded
- ExxonMobil Mobil Vaculine 1409
- Diamond Polymers DIAMALOY PC 1113 Impact Modified Polycarbonate
- Daikin DAI-EL G-551 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content
- Braskem LD5000A LDPE Blow Molding Polyethylene
- Gromax CCP PBT 3040-201 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved