Cresset Powers Cress-Alon™ A2700 2.7 r.v. Compounding Grade Nylon 6, Dry As Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Cresset Powers, Ltd |
| Trade Name | Cress-Alon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cresset Powers Cress-Alon™ A2700 2.7 r.v. Compounding Grade Nylon 6, Dry As Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Neat resin, for compounding.Information provided by Cresset Powers Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in³ | ASTM D792 |
| Apparent Bulk Density | >= 0.659 g/cc | >= 0.0238 lb/in³ | |
| Viscosity Measurement | 2.7 | 2.7 | Relative Viscosity |
| Melt Flow | 14 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 65.0 MPa | >= 9430 psi | ASTM D638 |
| Elongation at Yield | <= 6.0 % | <= 6.0 % | ASTM D638 |
| Flexural Yield Strength | >= 85.0 MPa | >= 12300 psi | ASTM D790 |
| Flexural Modulus | >= 2.50 GPa | >= 363 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.240 J/cm | >= 0.450 ft-lb/in | ASTM D256, Notch |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 - 224 °C | 428 - 435 °F | ASTM DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 55.0 °C | >= 131 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.080 % | <= 0.080 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extractables, wt% | <0.4 |
Users viewing this material also viewed the following:
- Osprey Metals Co452 Cobalt Alloy Powder (Grade 90% - 16)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling
- Fiberfil® PP-68/V2 Polypropylene Copolymer, Flame Retardant, UL94 V2
- H.C. Starck Amperit® 518.002 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Momentive Performance Materials IS806 Red Adhesive Sealant, General Purpose Paste
- SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copoly (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-KON DX05042 PC (Europe-Africa-Middle East)
- Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin
- Diamond Polymers ABS 3500 ELG Natural 1003 Injection Molding Grade, High Flow, Medium Impact, Low Gloss
- Elastocon TPE Technologies Elastocon® SMR1000 Thermoplastic Polyolefin Elastomer
Copyright © lookpolymers.com All Rights Reserved