Eurostar Staramide BST44 PA6, Impact Modified, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BST44 PA6, Impact Modified, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BST44 is a Low Temperature Impact Modified Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 2.00 %

@Temperature 23.0 °C
 2.00 %

@Temperature 73.4 °F
 50% RH; ISO 62
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ISO 2039-2
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break >= 100 %
>= 100 %
50 mm/min; ISO 527
Elongation at Yield 4.1 %
4.1 %
50 mm/min; ISO 527
Tensile Modulus 1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Yield Strength 60.0 MPa
8700 psi
2 mm/min; ISO 178
Flexural Modulus 1.60 GPa
232 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 50.0 kJ/m²

@Temperature -40.0 °C
 23.8 ft-lb/in²

@Temperature -40.0 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
65.0 kJ/m²

@Temperature -20.0 °C
 30.9 ft-lb/in²

@Temperature -4.00 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
75.0 kJ/m²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
Charpy Impact Unnotched >= 10.0 J/cm²

@Temperature 23.0 °C
 >= 47.6 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 179/1eU
>= 10.0 J/cm²

@Temperature -30.0 °C
 >= 47.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80x10x4 sp=62; ISO 179/1eA
7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 52.8 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature 23.0 - 60.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 160 °C
320 °F
B/120; ISO 306
165 °C
329 °F
B/50; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.017

@Frequency 1.00e+6 Hz
 0.017

@Frequency 1.00e+6 Hz
 IEC 60250
0.084

@Frequency 50.0 - 60.0 Hz
 0.084

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Comparative Tracking Index 575 V
575 V
IEC 60112
600 V
600 V
M; IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 230 °C
428 - 446 °F
Zone 1
Middle Barrel Temperature 230 - 240 °C
446 - 464 °F
Zone 2
Front Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 3
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %