Eurostar Star L POM D84 POM, Injection Molded
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L POM D84 POM, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L POM D84 is a PTFE/Proprietary Additive Lubricated, POM Copolymer Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.024 - 0.027 cm/cm @Thickness 4.00 mm |
0.024 - 0.027 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527 |
| Elongation at Break | 19 % | 19 % | ISO 527 |
| Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170.1 °C | 338.2 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 190 °C | 356 - 374 °F | |
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.10 % | 0.10 % |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion
- Radici Heraflex® A 40-11-91 TPS-SEBS Thermoplastic Elastomer
- Kazanorgsintez 162-281 Low Density Polyethylene Composition with Improved Processibility
- Inno-Comp INNOPOL® CS 2-9302 Elastomer Modified Polypropylene Block-Copolymer
- Sharadaa Ceramics PCF80 Precast Prefired Brick
- Samyang Tramid® 210 Polyamide, General Purpose
- Sawbones Third-Generation Simulated Cancellous Bone (Cellular)
- Denka VINYKON M1022A PVC, M grade for hard injection molding
- Arlon R37208T017 0.017" (0.432 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Liner
Copyright © lookpolymers.com All Rights Reserved