EMS-Grivory Grivory® ELX 40 HNZ TPA

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® ELX 40 HNZ TPA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grilon ELX 40 H NZ is a high viscosity, heat stabilized, impact modified, thermoplastic PA6 elastomer for extrusion blow moulding applications. Grilon ELX 40 H NZ has the following important properties: High melt strengthImpact resistant even at low temperaturesEasy processingProcessable on conventional as well as on 3 D-machinesSuitable for sequential blow molding process in combination with flexible grades Grilon ELX 40 H NZ is used typically as flexible part in the sequential blow molding technology in combination with a rigid PA6 grade such as Grilon RVZ-15H.1 or Grilon R 50 H NZ. Application examples are air ducts for turbo-chargers and engine air ducts.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in³	ISO 1183
Water Absorption	6.5 %	6.5 %	ISO 62
Moisture Absorption	2.00 %	2.00 %	ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm	0.0070 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	conditioned, 15s; ISO 868
	58	58	dry, 15s; ISO 868
Tensile Stress	16.0 MPa @Strain 50.0 %	2320 psi @Strain 50.0 %	conditioned; ISO 527-1/-2
	21.0 MPa @Strain 50.0 %	3050 psi @Strain 50.0 %	dry; ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	dry; ISO 527-1/-2
	>= 50 %	>= 50 %	conditioned; ISO 527-1/-2
Tensile Modulus	0.250 GPa	36.3 ksi	conditioned; ISO 527-1/-2
	0.550 GPa	79.8 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	dry; ISO 179/1eU
	NB	NB	conditioned; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	dry; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	NB	NB	dry; ISO 179/1eA
	NB	NB	conditioned; ISO 179/1eA
	2.50 J/cm² @Temperature 30.0 °C	11.9 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	2.50 J/cm² @Temperature 30.0 °C	11.9 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	160 µm/m-°C	88.9 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	170 µm/m-°C	94.4 µin/in-°F	ISO 11359-1/-2
Melting Point	210 °C	410 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	100 - 120 °C	212 - 248 °F	long term; EMS
	180 °C	356 °F	short term; EMS
Deflection Temperature at 0.46 MPa (66 psi)	60.0 °C	140 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	45.0 °C	113 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	conditioned; IEC 60093
	1.00e+11 ohm-cm	1.00e+11 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Strength	26.0 kV/mm	660 kV/in	conditioned; IEC 60243-1
	28.0 kV/mm	711 kV/in	dry; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Cooling and climate control
Electricals & Electronics	Cables & Tubes
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
Processing	Extrusion - blow molding
	Other Extrusion
Special Characteristics	High impact or impact modified
	Improved heat resistance