Eurostar Star L POM D11 POM, Injection Molded
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L POM D11 POM, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L POM D11 is Silicone Oil Lubricated, POM Copolymer Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.027 - 0.033 cm/cm @Thickness 4.00 mm |
0.027 - 0.033 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ISO 527 |
| Elongation at Break | 45 % | 45 % | ISO 527 |
| Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 120 kJ/m² | 57.1 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 190 °C | 356 - 374 °F | |
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.10 % | 0.10 % |
Users viewing this material also viewed the following:
- Poco Graphite HPD Semiconductor Grade Graphite
- Huntsman RenShape® SL 7820 Stereolithography Plastic
- Sylvin Technologies 8940-95 Natural PVC Extrusion Compound
- Solvay Specialty Polymers Polidan® T/A-LV Polyethylene, Crosslinked (XLPE)
- Saint-Gobain CHR® SG13-10(R) High Performance Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Borealis Supersmooth™ LE0550 Polyethylene Insulation Compound, Crosslinkable
- A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer
- A. Schulman POLYFORT™ FPP 3717 Talc Filled Homopolymer Polypropylene (39.6% Mineral Content)
Copyright © lookpolymers.com All Rights Reserved