Eurostar Star L PA6 30V D61 PA6, Glass Filled, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA6 30V D61 PA6, Glass Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA6 30V D61 is a PTFE/Silicone Oil Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 155 MPa | 22500 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 195 MPa | 28300 psi | ISO 178 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CQX30030 RTX Polypropylene, Mineral Reinforced, Scratch Resistant
- Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced
- Latrobe LSSâ„¢ 135M Nitriding Steel (ASTM A355 Class A)
- SolVin 250SB Polyvinyl Chloride General Purpose - Rigid
- SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66
- Unitika TERRAMAC TE-1030 Polylactic Acid (PLA)
- DSM Akulon® F232 PA6
- 3M Scotch-Weld™ 2141 Neoprene Rubber & Gasket Adhesive
- Aptek DI-STRATE 95212 Microwave/RF Foam Substrate
Copyright © lookpolymers.com All Rights Reserved