- Entec Hylex® P1010FR Polycarbonate
Entec Hylex® P1010FR Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hylex® P1010FR Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | 73°F, 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 152 °C | 305 °F | ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 0.0610 in, NA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | ASTM D542 |
| Haze | 0.90 - 1.0 % | 0.90 - 1.0 % | 125 mil; ASTM D1003 |
| Transmission, Visible | 87 - 89 % | 87 - 89 % | 125 mil; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | in Air, 0.125 in; ASTM D149 |
| Arc Resistance | 90 sec | 90 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Middle Barrel Temperature | 277 - 288 °C | 530 - 550 °F | |
| Front Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Nozzle Temperature | 277 - 299 °C | 530 - 570 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 76.7 - 93.3 °C | 170 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 6.89 - 12.4 MPa | 1000 - 1800 psi | |
| Back Pressure | 0.483 - 1.03 MPa | 70.0 - 150 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 700 to 1200 psi |
Users viewing this material also viewed the following:
- Process Technologies Inc BUNA-N Sanitary Gasket
- Nilit FRIANYL B63 KV40 Nylon 6 for injection molding, 40% glass ball reinforced
- Poco Graphite ZEE-2 Ion Implant Grade Graphite
- Arlon R3313X016-38 0.0165" (0.419 mm) Cured Silicone Rubber with Fiberglass Substrate 38" Wide (dis
- Huntsman HT 9664 Aromatic Amine
- Mitsubishi Xantar® MX 1081 Polycarbonate-10% Glass Reinforced
- H.C. Starck Amperit® 740.3 Aluminum Oxide (Al2O3)
- Lehmann & Voss PLASLUBE NY-1/TF/20/BK Polyamide 66, with PTFE
- Techmer ES HiFill FR® PBT GF30 FR 30% Glass Filled
- SABIC Innovative Plastics LNP Stat-kon ZE004 MODIFIED POYPHENYLENE (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved