Techmer ES HiFill FR® PBT FR-S
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Techmer ES |
| Trade Name | HiFill FR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill FR® PBT FR-S.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Flame Retardant and Non-BloomingProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 cm/cm @Thickness 3.17 mm |
0.025 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 56.5 MPa | 8200 psi | ASTM D638 |
| Elongation at Yield | 75 % | 75 % | ASTM D638 |
| Flexural Yield Strength | 101 MPa | 14700 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm |
0.700 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- DuPont Bynel® 41E623 Adhesive Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 19/CF/30 Polyamide 46, with carbon fiber
- Hybrid Plastics PO6C81.01 Nanoreinforced® Polyphenylene Oxide (PPO)
- Karina 10/1075-IE White Color Concentrate MBU
- Solvay Chemicals SPG Barium Hydroxide Monohydrate
- ExxonMobil Mobil Vaculine 525
- Arlon 51576XC15A 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Controltac™ FN180Cv3-10 Graphic Film
- 3M E-FIS Fire Barrier Expantrol Flexible Intumescent Strip
- Solvay RHODAFAC® RA-600 Surfactant
Copyright © lookpolymers.com All Rights Reserved