- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 290 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 290 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| RheTech Products GC8P200-00EG 8% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural, Extrusion Grade Applications: Extruded sheetWeather strippingInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-G10-[color]-1 Polycarbonate, 10% Glass Reinforced with Mold Release Polycarbonate, 10% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR1 Polycarbonate, 10% Glass Reinforced, Flame Retardant Polycarbonate, 10% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR1-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR2-[color]-4 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized with Mold Release Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pig.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PPX-GP6 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 290F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Ravago Manufacturing Americas Hylex® P1010FRMA Polycarbonate Polycarbonate, General Purpose, Flame RetardantInformation provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Multibase Multi-Pro® 4005 MI Polypropylene Mica Filled, 40% by weight.Features:Rigidity, HighImpact Resistance, GoodForms:PelletsProcessing Methods:Injection MoldingUses:Automotive ApplicationsInformation provided by Multibase |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR1-[color]-TFE Polycarbonate, 10% Glass Reinforced, PTFE, Flame Retardant, Wear Resistant Polycarbonate, 10% Glass Reinforced, PTFE, Flame Retardant, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, tes.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR2 Polycarbonate, 10% Glass Reinforced, Flame Retardant Polycarbonate, 10% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PC-HM-FR2-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Quantum Modified PPO - Noryl® Information provided by Quantum Advanced Engineering Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Fiberfil® J-60/10/FR Polypropylene Homopolymer, 10% Glass Reinforced, Flame Retardant Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HDPE 0226 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HDPE MM40 40% Mica Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mica Filler, 40% Filler by WeightFeatures: Chemically CoupledInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PP GF30 TL15 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: PTFE Lubricant (15%)Features: LubricatedInformation provided by TP Composites.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Teknor Apex Chemlon® 275H Nylon 6, Copolymer, Impact Modified Notes: Very high impact and elongation, low flexural modulus material for tubing and wire jacketing applications requiring a soft, flexible product; FMVSS Flammability: Passes, FMVSS 302Processing M.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HDPE LGF50 12 mm 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN100STL (COND, 50% RH) Nylon 66, Super Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | annealed; ASTM D648 |
| Lubrizol ISOPLAST™ 202EZ Engineering Thermoplastic Polyurethane Resin NSF Standard 61 CertifiedAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Ensinger Hydex™ 202 Rigid Polyurethane (PU) Hydex™ 202 is a totally rigid polyurethane resin that exhibits a broad range of chemical resistance, as well as superior impact and excellent mechanical properties. It can be used for any mechanic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Entec Hylex® P1310FR Polycarbonate Information provided by Ravago |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Entec Hylex® P1010FR Polycarbonate Information provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Asahi Kasei Thermylene® P1-10FG-8100 10% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Asahi Kasei Thermylene® P6-10FG-0100 10% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Aaron Industries AAROPRENE® GFPC 5020 Glass Filled Polycarbonate AAROPRENE® GFPC 5000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Polymer Resources PPX-GP6 Modified PPO, General Purpose with HDT of 290 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||