EMS-Grivory Grivory® XE 4216 black 9233 PA6T/66-GF30

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® XE 4216 black 9233 PA6T/66-GF30.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory XE 4216 black 9233 is a high heat stabilized, 30% glass fiber reinforced, semicrystalline, thermoplastic engineering material for injection molding. Polymer designation according to ISO: PA 6T/66+X According to ASTM: PPA, polyphthalamide. The main distinguishing feature of Grivory HT-PPA, when compared to other polyamides, is its good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. The special property profile of Grivory XE 4216 black 9233 makes it suitable for automotive parts with very high demands on heat stability. Parts of good surface quality are feasible. Grivory XE 4216 black 9233 is applicable for engine compartment and power-train applications such as:Charge air ductsCharge air cooler tanksAir intake silencersOil sumpsFunctional partsInformation provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Water Absorption	5.4 %	5.4 %	ISO 62
Moisture Absorption	2.10 %	2.10 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	210 MPa	30500 psi	conditioned; ISO 2039-1
	260 MPa	37700 psi	dry; ISO 2039-1
Tensile Strength at Break	150 MPa	21800 psi	conditioned; ISO 527-1/-2
	190 MPa	27600 psi	dry; ISO 527-1/-2
Elongation at Break	2.7 %	2.7 %	dry; ISO 527-1/-2
	2.7 %	2.7 %	conditioned; ISO 527-1/-2
Tensile Modulus	9.60 GPa	1390 ksi	conditioned; ISO 527-1/-2
	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	dry; ISO 179/1eU
	6.50 J/cm²	30.9 ft-lb/in²	conditioned; ISO 179/1eU
	4.50 J/cm² @Temperature 30.0 °C	21.4 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	4.50 J/cm² @Temperature 30.0 °C	21.4 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm²	4.28 ft-lb/in²	dry; ISO 179/1eA
	0.900 J/cm²	4.28 ft-lb/in²	conditioned; ISO 179/1eA
	0.700 J/cm² @Temperature 30.0 °C	3.33 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.700 J/cm² @Temperature 30.0 °C	3.33 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C	44.4 µin/in-°F	ISO 11359-1/-2
Melting Point	300 °C	572 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	150 °C	302 °F	long term; EMS
	250 °C	482 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	240 °C	464 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	155 °C	311 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Strength	45.0 kV/mm	1140 kV/in	dry; IEC 60243-1
	45.0 kV/mm	1140 kV/in	conditioned; IEC 60243-1
Comparative Tracking Index	525 V	525 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Fuel systems
	Hydraulic systems
	Interior
	Powertrain and Chassis
Electricals & Electronics	Connectors
	Electrical equipment
	Energy distribution
	Mobile phones and other portable devices
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Bio based Polyamide
	Co Polyamide
	Improved alcohol resistance
	Partially aromatic Polyamide
Special Characteristics	Improved heat resistance