EMS-Grivory Grivory® BS 23 PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BS 23 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 9.0 % | 9.0 % | ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 8.0 % | 8.0 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.30 GPa | 189 ksi | conditioned; ISO 527-1/-2 |
| 3.50 GPa | 508 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| 4.50 J/cm² @Temperature 30.0 °C |
21.4 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 0.400 J/cm² @Temperature 30.0 °C |
1.90 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 70.0 - 90.0 °C | 158 - 194 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | conditioned; IEC 60243-1 |
| 24.0 kV/mm | 610 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Interior | ||
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Processing | Injection Molding | |
| Product Attributes | Improved flowability and demoulding | |
| Nucleated |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 10 FRA 5 PA6, 10% glass fibre, flame retardant
- MarkeTech Repton 201 Aluminum Oxide
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- A. Schulman POLYBATCH™ Redwood 10416U Concentrate Based In LLDPE
- Loctite® 290 Wicking Grade Threadlocker
- CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Conditioned
- DuPont Performance Polymers Zytel® HTN 54G35EF BK420 Polyphthalamide (PPA) (Unverified Data**)
- Covestro Bayflex® XGT-100 Polyurethane Elastomeric RIM, 15% Milled Glass Filled, MDI-based 2-Component Liquid System
- BASF Lupranate® 224 Isocyanate
- BNZ Materials Bazelite 2500 LI Insulating Castable
Copyright © lookpolymers.com All Rights Reserved