EMS-Grivory Grivory® BGZ-15 PA6-GF15
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BGZ-15 PA6-GF15.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | conditioned; ISO 527-1/-2 |
| 120 MPa | 17400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.90 GPa | 421 ksi | conditioned; ISO 527-1/-2 |
| 5.40 GPa | 783 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | dry; ISO 179/1eU |
| 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | dry; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 500 V | 500 V | dry; IEC 60112 |
| 500 V | 500 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Granules | |
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- Idemitsu Kosan Xarec® N WA 7010 SPS, 10% Glass Filled (discontinued **)
- LG Chemical Lupoy 1200-15 Polycarbonate Resin
- Karina E 3600/004-IE MBU Brown Color Concentrate
- LG Chemical UHP-IPA ISOPROPYL ALCOHOL
- Sapco C 221 Steatite
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- Axiall HF-6597 Rigid PVC, Molding
- Ferro CF 7575 Low-Temperature Sealing
Copyright © lookpolymers.com All Rights Reserved