Diamond Polymers ABS VP-11 ELG

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ABS VP-11 ELG.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Extrusion Grade, Low Gloss, Flame RetardantInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0090 cm/cm
0.0040 - 0.0090 in/in
ASTM D955
Melt Flow 0.90 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.90 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 Procedure A Condition G; ASTM D1238
10.1 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 10.1 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 96
96
ASTM D785
Tensile Strength, Yield 39.14 MPa
5677 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.04 GPa
296 ksi
Tangent, chs 0.05 in/min; ASTM D790
Izod Impact, Notched 4.00 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 7.50 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 bar; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 72.2 °C
162 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
Vicat Softening Point 100.5 °C
212.9 °F
0.125 inch, 1 Kg; ASTM D1525
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 All Color
V-0

@Thickness 2.50 mm
 V-0

@Thickness 0.0984 in
 All Color
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 All Color
Optical Properties Metric English Comments
Gloss 42 %
42 %
60° View Angle; ASTM D523
Processing Properties Metric English Comments
Middle Barrel Temperature 200 - 220 °C
392 - 428 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Higher mold temperature provides a product with excellent surface finishing and less residual stress.
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 4.83 - 6.21 MPa
700 - 900 psi