- A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 2.295 GPa | 332.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Industeel URANUS® 35N 23.04 Duplex Stainless Steel with PREN = 24
- Latrobe Graph-Air® Cold Work Tool Steel (ASTM A10)
- Techmer ES HiFill® PA6/6 GF14 HS L BK 14% Glass Filled
- UCAR Carbon UCAR® CGW Isostatic Molded Graphite
- Polyram PlusTek RA702 Nylon 66 for Injection Molding, UV Stabilized
- Hexcel® HexWeb® CR-PAA™ 1/8-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb
- Eagle Brass 18665 MSP1, 1/2 Hard
- Chengdu Polyster 161 LPI Lenticular Lens Sheet, APET
- BASF Ultradur B 4406 G6 BKQ113 7110 30% Glass Filled PBT
- Devcon Wear Guard (High Load) Epoxy
Copyright © lookpolymers.com All Rights Reserved