E-Polymers TEKAMID® TA250G60W , 62% Glass Fiber Reinforced PA66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TA250G60W , 62% Glass Fiber Reinforced PA66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High strength, weather resistanceInformation provided by E-Polymers Co. Ltd.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792
Water Absorption 0.40 %
0.40 %
23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D786
Tensile Strength, Yield 210 MPa
30500 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Yield Strength 305 MPa
44200 psi
ASTM D790
Flexural Modulus 16.5 GPa
2390 ksi
ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
Izod Impact, Unnotched 70.0 J/cm

@Thickness 3.20 mm
 131 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Processing Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F