Physical Properties | Metric | English | Comments |
---|---|---|---|
Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | pellets; ISO 60 |
Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183-1 |
Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | ISO 62, 50% RH |
Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
Water Vapor Transmission | 15.0 g/m²/day @Thickness 0.100 mm |
0.966 g/100 in²/day @Thickness 0.00394 in |
85% RH, film; ISO 15106-1 |
Oxygen Transmission | 70.0 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
178 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
2760 cc/m²-24hr-bar; film; b.o. ISO 2556 |
70.0 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
178 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
700 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
Nitrogen Transmission | 13.0 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
33.0 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
130 cc/m²-24hr-bar; film; b.o. ISO 2556 |
13.0 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
33.0 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
510 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
Carbon Dioxide Transmission | 429 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
1090 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
16900 cc/m²-24hr-bar; film; b.o. ISO 2556 |
430 cc-mm/m²-24hr-atm @Thickness 0.100 mm |
1090 cc-mil/100 in²-24hr-atm @Thickness 0.00394 in |
4300 cc/m²-24hr-bar; film; b.o. ISO 2556 | |
Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Melt Flow | 6.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Puncture Resistance | 5600 N @Temperature 23.0 °C |
1260 lb (f) @Temperature 73.4 °F |
ISO 6603-2 |
6500 N @Temperature -30.0 °C |
1460 lb (f) @Temperature -22.0 °F |
ISO 6603-2 | |
Ball Indentation Hardness | 111 MPa | 16100 psi | ISO 2039-1 |
Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,-2 |
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-1,-2 |
Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
125 % | 125 % | 50 mm/min; b.o. ISO 527-1,-2 | |
Elongation at Yield | 6.3 % | 6.3 % | 50 mm/min; ISO 527-1,-2 |
Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527-1,-2 |
Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
Flexural Yield Strength | 72.0 MPa @Strain 3.50 % |
10400 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
Flexural Modulus | 2.35 GPa | 341 ksi | 2 mm/min; ISO 178 |
Izod Impact, Notched (ISO) | 16.0 kJ/m² @Thickness 3.20 mm, Temperature -30.0 °C |
7.61 ft-lb/in² @Thickness 0.126 in, Temperature -22.0 °F |
complete break; b.o. ISO 180-A |
90.0 kJ/m² @Thickness 3.20 mm, Temperature 23.0 °C |
42.8 ft-lb/in² @Thickness 0.126 in, Temperature 73.4 °F |
partial break; b.o. ISO 180-A | |
Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU | |
NB @Temperature -60.0 °C |
NB @Temperature -76.0 °F |
ISO 179-1eU | |
Charpy Impact, Notched | 1.80 J/cm² @Thickness 3.00 mm, Temperature -30.0 °C |
8.57 ft-lb/in² @Thickness 0.118 in, Temperature -22.0 °F |
complete break; ISO 7391/b.o. ISO 179-1eA |
8.00 J/cm² @Thickness 3.00 mm, Temperature 23.0 °C |
38.1 ft-lb/in² @Thickness 0.118 in, Temperature 73.4 °F |
partial break; ISO 7391/b.o. ISO 179-1eA | |
Puncture Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
70.0 J @Temperature -30.0 °C |
51.6 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | cross-flow; ISO 8302 |
Hot Ball Pressure Test | 140 °C | 284 °F | IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75-1,-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | ISO 75-1,-2 |
Vicat Softening Point | 149 °C @Load 5.10 kg |
300 °F @Load 11.2 lb |
50°C/h; ISO 306 |
150 °C @Load 5.10 kg |
302 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
Glass Transition Temp, Tg | 149 °C | 300 °F | 10°C/min; ISO 11357-1,-2 |
UL RTI, Electrical | 125 °C | 257 °F | UL 746B |
UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
||
Flash Point | 480 °C | 896 °F | ASTM D 1929 |
550 °C | 1020 °F | self ignition; ASTM D 1929 | |
Oxygen Index | 27 % | 27 % | Method A; ISO 4589-2 |
Glow Wire Test | 850 °C @Thickness 1.50 mm |
1560 °F @Thickness 0.0591 in |
b.o. EDF HN60 E.02 |
850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
b.o. EDF HN60 E.02 | |
850 °C @Thickness 1.00 mm |
1560 °F @Thickness 0.0394 in |
GWFI; IEC 60695-2-12 | |
850 °C @Thickness 1.50 mm |
1560 °F @Thickness 0.0591 in |
GWFI; IEC 60695-2-12 | |
850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
GWFI; IEC 60695-2-12 | |
875 °C @Thickness 1.00 mm |
1610 °F @Thickness 0.0394 in |
GWIT; IEC 60695-2-13 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm |
864 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Dissipation Factor | 0.00050 @Frequency 100 Hz |
0.00050 @Frequency 100 Hz |
IEC 60250 |
0.0095 @Frequency 1.00e+6 Hz |
0.0095 @Frequency 1.00e+6 Hz |
IEC 60250 | |
Comparative Tracking Index | 125 V | 125 V | CTI M; Solution B; IEC 60112 |
250 V | 250 V | Solution A; IEC 60112 |