DuPont Performance Polymers Zytel® 80G33HS1L BK104 Nylon 66 (Unverified Data**)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	DuPont Performance Polymers
Trade Name	Zytel®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Zytel® 80G33HS1L BK104 Nylon 66 (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L BK104 is a 33% glass fiber reinforced heat stabilized black polyamide 66 resin with outstanding impact resistance developed using DuPont Super Tough technology.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.33 g/cc	0.0480 lb/in³	DAM; ISO 1183
Water Absorption at Saturation	0.91 %	0.91 %	DAM; Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	DAM; ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	112 MPa	16200 psi	50%RH; ISO 527-1/-2
	148 MPa	21500 psi	DAM; ISO 527-1/-2
Elongation at Break	3.6 %	3.6 %	DAM; ISO 527-1/-2
	6.6 %	6.6 %	50%RH; ISO 527-1/-2
Tensile Modulus	6.50 GPa	943 ksi	50%RH; ISO 527-1/-2
	8.80 GPa	1280 ksi	DAM; ISO 527-1/-2
Flexural Strength	214 MPa	31000 psi	DAM; ISO 178
Flexural Modulus	7.60 GPa	1100 ksi	DAM; ISO 178
Shear Modulus	0.521 GPa @Temperature 150 °C	75.6 ksi @Temperature 302 °F	DAM; Dynamic; ISO 11403-1 -2
	0.6072 GPa @Temperature 110 °C	88.07 ksi @Temperature 230 °F	DAM; Dynamic; ISO 11403-1 -2
	1.1235 GPa @Temperature 60.0 °C	162.95 ksi @Temperature 140 °F	DAM; Dynamic; ISO 11403-1 -2
	1.5884 GPa @Temperature 10.0 °C	230.38 ksi @Temperature 50.0 °F	DAM; Dynamic; ISO 11403-1 -2
	1.6393 GPa @Temperature -20.0 °C	237.76 ksi @Temperature -4.00 °F	DAM; Dynamic; ISO 11403-1 -2
	1.941 GPa @Temperature -50.0 °C	281.5 ksi @Temperature -58.0 °F	DAM; Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO)	21.0 kJ/m²	9.99 ft-lb/in²	DAM; ISO 180/1A
	26.0 kJ/m²	12.4 ft-lb/in²	50%RH; ISO 180/1A
	15.0 kJ/m² @Temperature -40.0 °C	7.14 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 180/1A
	16.0 kJ/m² @Temperature -30.0 °C	7.61 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 180/1A
	17.0 kJ/m² @Temperature -30.0 °C	8.09 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 180/1A
Charpy Impact Unnotched	9.60 J/cm²	45.7 ft-lb/in²	50%RH; ISO 179/1eU
	9.70 J/cm²	46.2 ft-lb/in²	DAM; ISO 179/1eU
	9.70 J/cm² @Temperature -40.0 °C	46.2 ft-lb/in² @Temperature -40.0 °F	50%RH; ISO 179/1eU
	10.9 J/cm² @Temperature -40.0 °C	51.9 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 179/1eU
Charpy Impact, Notched	2.00 J/cm²	9.52 ft-lb/in²	DAM; ISO 179/1eA
	2.70 J/cm²	12.8 ft-lb/in²	50%RH; ISO 179/1eA
	1.70 J/cm² @Temperature -30.0 °C	8.09 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	1.80 J/cm² @Temperature -30.0 °C	8.57 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
	1.80 J/cm² @Temperature -40.0 °C	8.57 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 µm/m-°C	8.33 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	119 µm/m-°C	66.1 µin/in-°F	DAM; ISO 11359-1/-2
Melting Point	262 °C	504 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	261 °C	502 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	DAM; ISO 75-1/-2
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	DAM; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	400 V	400 V	DAM; IEC 60112

Descriptive Properties	Value	Comments
Emission of organic compounds	25.3 µgC/g	VDA 277
Odour	class 3	VDA 270
Part Marking Code	>PA66-IGF33<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66-IGF33
Special Characteristics	Heat stabilised or stable to heat