Material Notes:

Zytel® 79G13HSL BK039 is a 13 % glass reinforced, heat stabilized, lubricated slightly toughened black polyamide 66 for injection molding. It has improved impact resistance.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³	DAM; ISO 1183
Linear Mold Shrinkage, Flow	0.0050 cm/cm @Thickness 2.00 mm	0.0050 in/in @Thickness 0.0787 in	DAM; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0080 cm/cm @Thickness 2.00 mm	0.0080 in/in @Thickness 0.0787 in	DAM; ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	67.0 MPa @Temperature 23.0 °C	9720 psi @Temperature 73.4 °F	50%RH; ISO 527
	115 MPa @Temperature 23.0 °C	16700 psi @Temperature 73.4 °F	DAM; ISO 527
Elongation at Break	4.0 % @Temperature 23.0 °C	4.0 % @Temperature 73.4 °F	DAM; ISO 527
	10 % @Temperature 23.0 °C	10 % @Temperature 73.4 °F	50%RH; ISO 527
Tensile Modulus	3.70 GPa @Temperature 23.0 °C	537 ksi @Temperature 73.4 °F	50%RH; ISO 527
	5.10 GPa @Temperature 23.0 °C	740 ksi @Temperature 73.4 °F	DAM; ISO 527
Izod Impact, Notched (ISO)	7.50 kJ/m² @Temperature 23.0 °C	3.57 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 180/1A
	10.0 kJ/m² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	50%RH; ISO 180/1A
Charpy Impact Unnotched	5.40 J/cm² @Temperature -30.0 °C	25.7 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eU
	5.90 J/cm² @Temperature 23.0 °C	28.1 ft-lb/in² @Temperature 73.4 °F	50%RH; ISO 179/1eU
	5.90 J/cm² @Temperature -30.0 °C	28.1 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eU
	6.70 J/cm² @Temperature 23.0 °C	31.9 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	50%RH; ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	262 °C	504 °F	10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	260 °C	500 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	240 °C	464 °F	DAM; ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; UL94
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	DAM; UL94

Processing Properties	Metric	English	Comments
Melt Temperature	285 - 305 °C	545 - 581 °F	DAM
	295 °C	563 °F	DAM; Optimum
Drying Temperature	80.0 °C	176 °F	DAM
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	DAM
Moisture Content	<= 0.20 %	<= 0.20 %	DAM

Descriptive Properties	Value	Comments
Forms	Pellets	DAM
Generic	Nylon 66	DAM
Material Status	Current	DAM
Processing Method	Injection Molding	DAM
Product Category	Glass Reinforced Resins	DAM
	Toughened Resins	DAM
RoHS Compliance	Contact Manufacturer	DAM