DuPont Performance Polymers Zytel® 158L NC010 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 158L NC010 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® 158L NC010 is an intermediate viscosity, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
DAM; ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
DAM; ISO 1183
Water Absorption 0.25 %

@Temperature 23.0 °C
 0.25 %

@Temperature 73.4 °F
 Immersion 24h; DAM; ASTM D570
1.3 %

@Temperature 23.0 °C
 1.3 %

@Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 Saturation; DAM; ASTM D570
Linear Mold Shrinkage 0.011 cm/cm

@Thickness 3.20 mm
 0.011 in/in

@Thickness 0.126 in
 Flow; DAM
Linear Mold Shrinkage, Flow 0.013 cm/cm

@Thickness 2.00 mm
 0.013 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 2.00 mm
 0.014 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
50%RH; ASTM D785
114
114
DAM; ASTM D785
Tensile Strength 30.0 MPa

@Temperature 121 °C
 4350 psi

@Temperature 250 °F
 50%RH; ASTM D638
37.0 MPa

@Temperature 77.0 °C
 5370 psi

@Temperature 171 °F
 50%RH; ASTM D638
41.0 MPa

@Temperature 77.0 °C
 5950 psi

@Temperature 171 °F
 DAM; ASTM D638
52.0 MPa

@Temperature 23.0 °C
 7540 psi

@Temperature 73.4 °F
 50%RH; ASTM D638
61.0 MPa

@Temperature 23.0 °C
 8850 psi

@Temperature 73.4 °F
 DAM; ASTM D638
93.0 MPa

@Temperature -40.0 °C
 13500 psi

@Temperature -40.0 °F
 DAM; ASTM D638
93.0 MPa

@Temperature -40.0 °C
 13500 psi

@Temperature -40.0 °F
 50%RH; ASTM D638
Tensile Strength, Yield 17.0 MPa

@Temperature 121 °C
 2470 psi

@Temperature 250 °F
 50%RH; ASTM D638
30.0 MPa

@Temperature 77.0 °C
 4350 psi

@Temperature 171 °F
 DAM; ASTM D638
35.0 MPa

@Temperature 77.0 °C
 5080 psi

@Temperature 171 °F
 50%RH; ASTM D638
51.0 MPa

@Temperature 23.0 °C
 7400 psi

@Temperature 73.4 °F
 50%RH; ASTM D638
52.0 MPa

@Temperature 23.0 °C
 7540 psi

@Temperature 73.4 °F
 50%RH; ISO 527
61.0 MPa

@Temperature 23.0 °C
 8850 psi

@Temperature 73.4 °F
 DAM; ASTM D638
62.0 MPa

@Temperature 23.0 °C
 8990 psi

@Temperature 73.4 °F
 DAM; ISO 527
93.0 MPa

@Temperature -40.0 °C
 13500 psi

@Temperature -40.0 °F
 50%RH; ASTM D638
94.0 MPa

@Temperature -40.0 °C
 13600 psi

@Temperature -40.0 °F
 DAM; ASTM D638
Elongation at Break 15 %

@Temperature -40.0 °C
 15 %

@Temperature -40.0 °F
 DAM; ASTM D638
30 %

@Temperature -40.0 °C
 30 %

@Temperature -40.0 °F
 50%RH; ASTM D638
35 %

@Temperature 23.0 °C
 35 %

@Temperature 73.4 °F
 DAM; nominal; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50%RH; nominal; ISO 527
>= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
 50%RH; nominal; ISO 527
150 %

@Temperature 23.0 °C
 150 %

@Temperature 73.4 °F
 DAM; ASTM D638
250 %

@Temperature 121 °C
 250 %

@Temperature 250 °F
 50%RH; ASTM D638
>= 300 %

@Temperature 23.0 °C
 >= 300 %

@Temperature 73.4 °F
 50%RH; ASTM D638
>= 300 %

@Temperature 77.0 °C
 >= 300 %

@Temperature 171 °F
 50%RH; ASTM D638
>= 300 %

@Temperature 77.0 °C
 >= 300 %

@Temperature 171 °F
 DAM; ASTM D638
Elongation at Yield 4.5 %

@Temperature 23.0 °C
 4.5 %

@Temperature 73.4 °F
 DAM; ISO 527
7.0 %

@Temperature 23.0 °C
 7.0 %

@Temperature 73.4 °F
 DAM; ASTM D638
8.0 %

@Temperature -40.0 °C
 8.0 %

@Temperature -40.0 °F
 DAM; ASTM D638
14 %

@Temperature -40.0 °C
 14 %

@Temperature -40.0 °F
 50%RH; ASTM D638
19 %

@Temperature 23.0 °C
 19 %

@Temperature 73.4 °F
 50%RH; ISO 527
30 %

@Temperature 77.0 °C
 30 %

@Temperature 171 °F
 DAM; ASTM D638
40 %

@Temperature 23.0 °C
 40 %

@Temperature 73.4 °F
 50%RH; ASTM D638
Tensile Modulus 1.50 GPa

@Temperature 23.0 °C
 218 ksi

@Temperature 73.4 °F
 50%RH; ISO 527
2.40 GPa

@Temperature 23.0 °C
 348 ksi

@Temperature 73.4 °F
 DAM; ISO 527
Flexural Modulus 0.300 GPa

@Temperature 121 °C
 43.5 ksi

@Temperature 250 °F
 50%RH; ASTM D790
0.330 GPa

@Temperature 121 °C
 47.9 ksi

@Temperature 250 °F
 DAM; ASTM D790
0.380 GPa

@Temperature 77.0 °C
 55.1 ksi

@Temperature 171 °F
 50%RH; ASTM D790
0.415 GPa

@Temperature 77.0 °C
 60.2 ksi

@Temperature 171 °F
 DAM; ASTM D790
1.24 GPa

@Temperature 23.0 °C
 180 ksi

@Temperature 73.4 °F
 50%RH; ASTM D790
1.45 GPa

@Temperature 23.0 °C
 210 ksi

@Temperature 73.4 °F
 50%RH; ISO 178
2.03 GPa

@Temperature 23.0 °C
 294 ksi

@Temperature 73.4 °F
 DAM; ASTM D790
2.05 GPa

@Temperature 23.0 °C
 297 ksi

@Temperature 73.4 °F
 DAM; ISO 178
2.34 GPa

@Temperature -40.0 °C
 339 ksi

@Temperature -40.0 °F
 DAM; ASTM D790
2.76 GPa

@Temperature -40.0 °C
 400 ksi

@Temperature -40.0 °F
 50%RH; ASTM D790
Shear Strength 56.0 MPa

@Temperature 23.0 °C
 8120 psi

@Temperature 73.4 °F
 50%RH; ASTM D732
59.0 MPa

@Temperature 23.0 °C
 8560 psi

@Temperature 73.4 °F
 DAM; ASTM D732
Izod Impact, Notched 0.320 J/cm

@Temperature -40.0 °C
 0.599 ft-lb/in

@Temperature -40.0 °F
 50%RH; ASTM D256
0.480 J/cm

@Temperature -40.0 °C
 0.899 ft-lb/in

@Temperature -40.0 °F
 DAM; ASTM D256
0.530 J/cm

@Temperature 23.0 °C
 0.993 ft-lb/in

@Temperature 73.4 °F
 DAM; ASTM D256
0.750 J/cm

@Temperature 23.0 °C
 1.41 ft-lb/in

@Temperature 73.4 °F
 50%RH; ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1A
4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 50%RH; ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 50%RH; ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 DAM; ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 DAM; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 50%RH; ISO 179/1eA
Tensile Impact Strength 154 kJ/m²

@Temperature 23.0 °C
 73.3 ft-lb/in²

@Temperature 73.4 °F
 DAM; Short specimen; ASTM D1822