DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 157HSL BK010 is a heat stabilized, weatherable, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | DAM; ASTM D792 |
| Density | 1.07 g/cc | 0.0387 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
Immersion 24h; DAM; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DAM; ASTM D785 |
| Tensile Strength | 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
50%RH; ASTM D638 |
| 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
DAM; ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa @Temperature 23.0 °C |
7690 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 65.0 MPa @Temperature 23.0 °C |
9430 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 22 % @Temperature 23.0 °C |
22 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 |
| 30 % @Temperature 23.0 °C |
30 % @Temperature 73.4 °F |
DAM; ASTM D638 | |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 | |
| 75 % @Temperature 23.0 °C |
75 % @Temperature 73.4 °F |
50%RH; ASTM D638 | |
| Elongation at Yield | 4.4 % @Temperature 23.0 °C |
4.4 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 18 % @Temperature 23.0 °C |
18 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Strength | 44.0 MPa @Temperature 23.0 °C |
6380 psi @Temperature 73.4 °F |
50%RH; ISO 178 |
| 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Flexural Modulus | 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
50%RH; ASTM D790 |
| 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
50%RH; ISO 178 | |
| 2.18 GPa @Temperature 23.0 °C |
316 ksi @Temperature 73.4 °F |
DAM; ASTM D790 | |
| 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C |
0.806 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
50%RH; ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
50%RH; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 218 °C | 424 °F | DAM; ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | DAM; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ASTM D648 |
| 62.0 °C | 144 °F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 105 °C @Thickness 3.00 mm |
221 °F @Thickness 0.118 in |
DAM; UL 746B |
| 105 °C @Thickness 0.860 mm |
221 °F @Thickness 0.0339 in |
DAM; UL 746B | |
| 105 °C @Thickness 1.50 mm |
221 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.860 mm |
149 °F @Thickness 0.0339 in |
DAM; UL 746B |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B |
| 65.0 °C @Thickness 0.860 mm |
149 °F @Thickness 0.0339 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
DAM; UL94 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C |
>= 600 V @Temperature 73.4 °F |
DAM; UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | DAM; Optimum |
| 230 - 290 °C | 446 - 554 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Carbon Black | DAM |
| Heat Stabilizer | DAM | |
| Lubricant | DAM | |
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Extrudable - Blown Film | Yes | DAM |
| Extrudable - Coating | Yes | DAM |
| Extrudable - Filament | Yes | DAM |
| Extrudable - Hose | Yes | DAM |
| Extrudable - Sheet | Yes | DAM |
| Extrudable - Tubing | Yes | DAM |
| Extrudable - Wire and Cable | Yes | DAM |
| Extrusion Blow Moldable | Yes | DAM |
| Features | Chemical Resistance, Good | DAM |
| Heat Aging Resistance, Good | DAM | |
| Lubricated | DAM | |
| Lubricated | DAM | |
| Wear Resistance, Good | DAM | |
| Weather Resistance, Good | DAM | |
| Forms | Pellets | DAM |
| Generic | Nylon 612 | DAM |
| Heat Stabilized | Yes | DAM |
| Injection Blow Moldable | Yes | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA612< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA612 | DAM |
| Processing Method | Extrusion | DAM |
| Injection Molding | DAM | |
| Product Category | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| UV Resistant/Weatherable Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA612 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| Uses | Automotive Applications | DAM |
Users viewing this material also viewed the following:
- KB Alloys Tibor® 5% Ti - 0.1% B Titanium Boron Aluminum Alloy
- LG Chemical Lutex 120 NBR Latex
- Taiwan Sheen Soon Sheenthane® AH-670 TPU for Hotmelt Adhesive
- Sharadaa Ceramics 29 Insulation Bricks-ASTM
- SABIC Innovative Plastics LNP STAT-KON RE002 PA 66
- Eifeler Coatings Technology SUCASLIDE® DLC coating
- Dow LDPE 527A Low Density Polyethylene, Blown Film Grade
- C.O.I.M. PLAXTER® P 72 Polymeric Plasticizer
- Ashley Polymers Ashlene® D870, D870L, Transparent Amorphous Nylon
- Arkema Group EVATANE® 28-420 Copolymer Ethylene - Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved