SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| 1.301 g/cc | 0.04700 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
| 130 MPa | 18900 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Tensile Modulus | 8.29 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| 8.83 GPa | 1280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 187 MPa | 27100 psi | ISO 178 |
| 204 MPa | 29600 psi | ASTM D790 | |
| Flexural Modulus | 7.11 GPa | 1030 ksi | ISO 178 |
| 8.08 GPa | 1170 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.88 J/cm | 12.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm |
387 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Radici Radilon® S RV330 (cond.) Nylon 6
- M. Holland Company LL104 LLDPE (discontinued **)
- Chevron Phillips Ryton® P-4 Polyphenylene Sulfide Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1301/CF/20 PPS, linear, with carbon fiber
- Lanxess Durethan® B 40 F 000000 Nylon 6, Film Grade
- Techmer ES Plastiblend® PC/ABS 88 GF 10% Glass Filled
- Chase Plastics CP Pryme® A300 BK General Purpose (Utility) ABS Molding Resin
- ATI Allegheny Ludlum 310S Austenitic Stainless Steel
- Beijing Chemical Industry KAIFA® 301-G10F PBT Resin
Copyright © lookpolymers.com All Rights Reserved