DuPont Performance Polymers Minlon® EFE6096 GY090A Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Minlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Minlon® EFE6096 GY090A Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Minlon® EFE6096 GY090A is a 15% mineral reinforced impact modified nylon 66 resin.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DAM; ISO 1183 |
| Filler Content | 15 % | 15 % | DAM |
| Water Absorption | 2.1 % @Temperature 23.0 °C |
2.1 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 7.7 % @Temperature 23.0 °C |
7.7 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 2.00 mm |
0.011 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm |
0.011 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa @Temperature 23.0 °C |
7540 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 76.0 MPa @Temperature 23.0 °C |
11000 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Tensile Strength | 79.0 MPa @Temperature 23.0 °C |
11500 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Elongation at Break | 17 % @Temperature 23.0 °C |
17 % @Temperature 73.4 °F |
DAM; ASTM D638 |
| 21 % @Temperature 23.0 °C |
21 % @Temperature 73.4 °F |
DAM; ISO 527 | |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| 52 % @Temperature 23.0 °C |
52 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Modulus | 3.72 GPa @Temperature 23.0 °C |
540 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | DAM |
| 295 °C | 563 °F | DAM; Optimum | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Mineral filler | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66-IMD15< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| Resin Identification | PA66-IMD15 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Ohio Carbon Blank OCB TTK-4C EDM Grade Graphite
- Network Polymers NPP 3514
- DSM Akulon® Ultraflow™ K-FHGM44 Nylon 6-40% Glass and Mineral Reinforced (European and Asian Grade) (Dry) (di
- Iran Petrochemical (PCC) TPC - 422 FC Expandable Polystyrene
- SABIC Innovative Plastics Xenoy® X4810 PBT+PC
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Fainplast Compounds HAX HF 22G Halogen Free PVC
- CMW® DSC Copper with Dispersed Aluminum Oxide
- Dow PAPI™ 580 N Polymeric MDI
- DuPont Nucrel® 0609HS Ethylene-Methacrylic Acid Copolymer Resin for Extrusion Coating/Laminating (discontinue
Copyright © lookpolymers.com All Rights Reserved