DuPont Performance Polymers Crastin® T835FRUV NC010 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Crastin® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Crastin® T835FRUV NC010 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crastin® T835FRUV NC010 is a 5% glass fiber reinforced, toughened, flame retardant polybutylene terephthalate resin for injection molding. (precommercial code = Crastin® CE2402)Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Filler Content | 5.0 % | 5.0 % | |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 3.20 mm |
0.013 in/in @Thickness 0.126 in |
Transverse |
| 0.014 cm/cm @Thickness 3.20 mm |
0.014 in/in @Thickness 0.126 in |
Flow |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
ASTM D638 |
| 62.0 MPa @Temperature 23.0 °C |
8990 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
ASTM D638 |
| 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
ISO 527 | |
| Tensile Modulus | 3.40 GPa @Temperature 23.0 °C |
493 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
ISO 178 |
| 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Izod Impact, Notched | 1.50 J/cm @Temperature 23.0 °C |
2.81 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 130 °C @Thickness 0.800 mm |
266 °F @Thickness 0.0315 in |
UL 746B |
| 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
UL 746B | |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL 746B | |
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.800 mm |
266 °F @Thickness 0.0315 in |
UL 746B |
| 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
UL 746B | |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL 746B | |
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.800 mm |
266 °F @Thickness 0.0315 in |
UL 746B |
| 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
UL 746B | |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL 746B | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 | |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
IEC 60695-11-10 | |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL94 | |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL94 | |
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Optimum |
| 240 - 260 °C | 464 - 500 °F | ||
| Mold Temperature | 80.0 °C | 176 °F | optimum |
| 30.0 - 130 °C | 86.0 - 266 °F | ||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.040 % | <= 0.040 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Drying Recommended | Yes | |
| Filler | Glass fiber reinforcement | |
| Generic | PBT | |
| Material Status | Current | |
| Part Marking Code | >PBT-IGF5FR(17)< | ISO 11469 |
| Polymer Family | Polyester | |
| Polymer Type | PBT | |
| Product Category | Flame Retardant Resins | |
| Glass Reinforced Resins | ||
| Toughened Resins | ||
| UV Resistant/Weatherable Resins | ||
| Resin Identification | PBT-IGF5FR(17) | ISO 1043 |
| RoHS Compliance | Contact Manufacturer |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 21 Ethylene Vinyl Acetate Copolymer - Injection Molding
- Overview of materials for Nylon 612, Impact Modified
- LG Chemical AF312 ABS, Flame Retardant
- Stir SpA AF 80 3 GEC (PVC)
- Samsung Cheil Industries Starex® VH-0819 ABS, Unreinforced FR
- UBE UBEPOL BR150 Synthetic Rubber (Compound)
- Total 8183 HDPE, blow molding
- ChevronTexaco Gear Compounds EP, ISO 460
- Dow LDPE 955I Low Density Polyethylene
- Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved