DuPont Bexloy® AXW502NC010 Modified Ionomer Resin (discontinued **)
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Bexloy® AXW502NC010 Modified Ionomer Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A modified ionomer resin engineered for injection molded exterior automotive applications.Availability: North AmericaInformation provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 - ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 - ISO 527-2 |
| Elongation at Break | 400 % | 400 % | ASTM D638 - ISO 527-2 |
| Flexural Modulus | 0.7580 GPa | 109.9 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Temperature -30.0 °C |
16.0 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J @Temperature -30.0 °C |
26.7 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Impact Test | 18.0 J | 13.2 ft-lb | Rheometric |
| 21.9 J @Temperature 22.8 °C |
16.2 ft-lb @Temperature 73.0 °F |
Rheometric, 5mph, 1/2" diameter tup, 3" diameter ring | |
| Tear Strength | 149 kN/m | 850 pli | At 73°F; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 76.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
42.2 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM E831 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 238 - 271 °C | 460 - 520 °F | |
| Melt Temperature | 238 - 288 °C | 460 - 550 °F | |
| Mold Temperature | 15.6 - 60.0 °C | 60.0 - 140 °F | |
| Drying Temperature | 60.0 - 79.4 °C | 140 - 175 °F | |
| Moisture Content | <= 0.080 % | <= 0.080 % | |
| Back Pressure | >= 0.345 MPa | >= 50.0 psi | no units given |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Sag, 82°C | 13 mm | ASTM D3769 |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A L Natural Polyamide 66 (Nylon 66)
- Lehmann & Voss LUVOCOM® 50-0789 Polycarbonate, with carbon fiber, easy flowing
- Sekisui PIOCELAN LSP-40EB Moldable Polymer Foam
- Teknor Apex APEX® 3202-80 Polyvinyl Chloride, Flexible
- Hexcel® HexPly® 954-2A Curing Cyanate Resin, IM7 Fiber
- DSM Arnite® AV2 372 PET-35% Glass Reinforced (European and Asian Grade)
- Aclo Accuguard Polypropylene CP1467V2CSL Copolymer Flame Retardant Copper Stabilized
- Barlog Plastics KEBAFLEX P D72.1 Polyester-Elastomer, Shore D75
- Braskem LF0720/20AF Blown Film Extrusion Linear Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved