Dow ELITE™ 5100G Enhanced Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name ELITE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow ELITE™ 5100G Enhanced Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
™ 5100G is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers excellent impact strength, good tensile and puncture properties for thick and thin gauge industrial and consumer blown film applications. This resin exhibits higher hot tack strengths than LLDPE, making it ideal for automated packaging applications.Information provided by Dow
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 0.85 g/10 min
0.85 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.80 MPa
1712 psi
ASTM D882
Film Tensile Strength at Yield, TD 12.5 MPa
1810 psi
ASTM D882
Film Elongation at Break, MD 595 %
595 %
ASTM D882
Film Elongation at Break, TD 652 %
652 %
ASTM D882
Secant Modulus, MD 0.2216 GPa
32.14 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.2575 GPa
37.35 ksi
2% Secant; ASTM D882
Impact 24
24
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
249
249
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy 9.04 J
6.67 ft-lb
Dow Method
Elmendorf Tear Strength MD 707 g
707 g
ASTM D1922
Elmendorf Tear Strength TD 1033 g
1033 g
ASTM D1922
Elmendorf Tear Strength, MD 13.92 g/micron
353.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 20.33 g/micron
516.5 g/mil
ASTM D1922
Dart Drop Test 780 g
1.72 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 57.27 MPa
8307 psi
ASTM D882
Film Tensile Strength at Break, TD 53.47 MPa
7755 psi
ASTM D882
Heat Seal Strength Initiation Temperature 106 °C
223 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Dow Method (DSC)
Vicat Softening Point 105 °C
221 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 10 %
10 %
ASTM D1003
Gloss 67 %
67 %
45°; ASTM D2457