- Teknor Apex Chemlon® 133 GVH Nylon 66, 30% Glass Fiber Reinforced
Teknor Apex Chemlon® 133 GVH Nylon 66, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 133 GVH Nylon 66, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Excellent for connectors and electrical parts; Flammability: Passes, FMVSS 302 Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 134 MPa | 19500 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.4 µm/m-°C | 28.0 µin/in-°F | ASTM D696 |
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 470 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.00 mm |
380 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 300 V | 300 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Front Barrel Temperature | 263 - 285 °C | 505 - 545 °F | |
| Nozzle Temperature | 263 - 285 °C | 505 - 545 °F | |
| Melt Temperature | 263 - 285 °C | 505 - 545 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 130 CLEAR FLEXIBLE (100 Viscosity) Rapid Bonding Adhesive
- Polimeri Europa Europrene® SOL TH 2315 Styrene - Ethylene / Butylene Block Copolymer
- Momentive Performance Materials NX5 Boron Nitride (BN) Powder
- Teknor Apex Sinvicomp SIM 5029 Polyvinyl Chloride, Flexible
- Williams Advanced Alloys Wambraze™ WB361 Solder
- UBE Tyranno Grade LoxM Ceramic High Temperature Fiber
- Chosun Refractories A-4 Insulating Firebrick
- Channel Industries 5804 Lead Zirconate Titanate Piezoelectric
- Compuestos Dominicanos Polycom CO-160355 PVC Compound
Copyright © lookpolymers.com All Rights Reserved