Diamond Polymers SE 3 HH
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers SE 3 HH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High Heat ABSInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.70 g/10 min @Load 10.0 kg, Temperature 220 °C |
0.70 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.1 MPa | 7550 psi | chs 2 in/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Flexural Modulus | 2.71 GPa | 393 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 1.92 J/cm | 3.60 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.2 °C | 207 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| 105 °C | 221 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 113 °C | 235 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IR2110 PC (Europe-Africa-Middle East)
- Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced
- Taiwan PU Corporation UR80 Polyester Urethane Rubber
- Tra-Con Tra-Bond RO7 Radio Opaque Epoxy Adhesive
- A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene
- DSM Arnite® TV4 230 S PBT-GF15 FR(17)
- Fainplast Compounds HG 78 Flexible PVC, Sheathing for High Temperatures
- AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Deep Drawing Steel (DDS Type B), Standard Grade
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
Copyright © lookpolymers.com All Rights Reserved