Diamond Polymers ABS TR-7
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS TR-7.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High Heat ABSInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.90 g/10 min @Load 10.0 kg, Temperature 220 °C |
0.90 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 340 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 0.25 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP4REU PC (Europe-Africa-Middle East)
- MarkeTech Yttrium Vanadate (YVO4) Fiber Optic Crystal
- Loxim 140 01V0 Polycarbonate, 40% Glass Filled, Flame Retardant
- H.C. Starck Amperit® 155.086 Titanium (Ti)
- SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East)
- Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, Conditioned
- Suqian Unitechem Antioxidant 168
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 400 Gauge
- Arlon 25188T017 Silicone Rubber/Laminated ETFE Film
- Arlon 51946C015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved