- Quantum PEI - Ultem® 30% Glass Fiber Filled
Quantum PEI - Ultem® 30% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 30% Glass Fiber |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum PEI - Ultem® 30% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.16 % | 0.16 % | ASTM D570 |
| Water Absorption at Saturation | 0.90 % | 0.90 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 114 | 114 | ASTM D785 |
| Hardness, Rockwell R | 127 | 127 | ASTM D785 |
| Hardness, Shore D | 86 | 86 | ASTM 2240 |
| Tensile Strength | 169 MPa | 24500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Compressive Strength | 212 MPa | 30700 psi | ASTM D695 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.24 | 0.24 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.259 W/m-K | 1.80 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 228 °C | 442 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 171 °C | 340 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+16 ohm-cm | 3.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 30.3 kV/mm | 770 kV/in | ASTM D149 |
| Dissipation Factor | 0.0015 @Frequency 1.00e+6 Hz |
0.0015 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | no |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 600 Zip 0 Black 13 Polyamide 6 Alloy (Nylon 6 Alloy)
- Hong Kun Group 2,2,6,6-Tetramethyl-piperidine-1-oxyl(TEMPO) Additive
- Lehmann & Voss LUVOCOM® 1850-7942 PBT, with PTFE, lubricant modified
- Solvay ALKAMULS® EL 719/100 Surfactant
- ExxonMobil Escorene® LD 768.MJ Molding, extrusion and compounding resin
- DuPont™ Tedlar® TTR10BG3 Transparent Polyvinyl Fluoride Film
- Entec Hyrene® PS-HI 3/2 High Impact Polystyrene
- Alliance Polymers Viprene™ G75A-32U-NAT Thermoplastic Vulcanizate Elastomer
- 3M AC-236 Class A-1/2 Aerospace Sealant
Copyright © lookpolymers.com All Rights Reserved