Diamond Polymers ABS 3501E Natural 1050
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3501E Natural 1050.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 340 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
6.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 93.9 °C | 201 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 104 °C | 219 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- RheTech Products GC10P100-01 10% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
- Eastman Tenite 264-10 CAB Cellulose Acetate Butyrate (discontinued **)
- Williams Advanced Alloys WS232 Solder
- Devcon Tile Adhesive Epoxy
- BASF Triethylamine TEA
- Fainplast Compounds PM 80/A Flexible PVC, Lead Free
- SYNTHOS Krasten® 171 General Purpose Polystyrene
- A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C)
- LATI Latimass 62-05 D040 PA6
Copyright © lookpolymers.com All Rights Reserved