- Acrylonitrile Butadiene Styrene (ABS), Molded
- Diamond Polymers ABS 1100
Diamond Polymers ABS 1100
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 1100.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding Grade, Extra High GlossInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 13.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
13.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.10 GPa | 450 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.500 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 92.8 °C | 199 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 104 °C | 219 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- NYC YT3W Y2O3 Powder
- Ravago Manufacturing Americas Hybrid S466 ABS + Polycarbonate Alloy
- Quadrant EPP Duratron® PAI T5530 Compression Molded Glass Reinforced Polyamide-imide (ASTM Product Data Sheet)
- Hong Kun Group 4'-Chloro-3'-nitroacetophenone Pharmaceutical Intermediate
- SABIC Innovative Plastics ULTEM CRS5311 PEI (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF2919 Fluoropolymer Tape
- Styron XZ 92091.01 Cross-Linking SB
- Teknor Apex Telcar® TL-91-T3056D-75 Thermoplastic Elastomer
- Overview of materials for Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved