Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Denka MALECCA K-090 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Denka
Trade Name MALECCA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka MALECCA K-090 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had defects in terms of moldability, thermal stability, and impact resistance.ApplicationsMobile phonesvehicle-mounted audio equipmentautomotive interior componentshome electric appliancesOA equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Melt Flow 12 g/10 min

@Load 10.0 kg,
Temperature 220 °C
12 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ISO 2039-2
114
114
ASTM D785
Tensile Strength at Break 43.0 MPa
6240 psi
ASTM D638
49.0 MPa
7110 psi
50mm/min; ISO 527-2
Tensile Strength, Yield 38.0 MPa
5510 psi
ISO 527-2
Elongation at Break 30 %
30 %
ISO 527-2
Tensile Modulus 2.60 GPa
377 ksi
1mm/min; ISO 527-1
Flexural Strength 72.0 MPa
10400 psi
15mm/min; ASTM D790
74.0 MPa
10700 psi
ISO 178
Flexural Modulus 2.45 GPa
355 ksi
15mm/min; ASTM D790
2.55 GPa
370 ksi
2mm/min; ISO 178
Izod Impact, Notched 2.16 J/cm

@Temperature 23.0 °C
4.05 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
ISO 75-2
97.0 °C
207 °F
ASTM D648
Vicat Softening Point 107 °C
225 °F
50N; ISO 306
Flammability, UL94 HB
HB