- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- HDPE
- LG Chemical LUTENE-H FE0070 HDPE
LG Chemical LUTENE-H FE0070 HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE-H |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE-H FE0070 HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUTENE-H FE0070 is mainly intended for the extrusion of blown film with high mechanical properties for the manufacture of "T-Shirt" grocery sacks, can liners. Especially, LUTENE-H FE0070 resin can be relied upon for excellent performance under heavy load conditions. LUTENE-H FE0070 resin is a high molecular weight, high density polyethylene. The film produced from this resin characteristically exhibits high tensile strength, stiffness, impact strength and barrier properties. It can be down-gauged to as low as 10 micro-m.Applications: Merchandise bags, consumer trash bags, industrial and institutional liners.CAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.953 g/cc | 0.953 g/cc | ASTM D1505 |
| Thickness | 10.0 microns | 0.394 mil | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 37.3 MPa | 5410 psi | ASTM D822 |
| Film Tensile Strength at Yield, TD | 35.3 MPa | 5120 psi | ASTM D822 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D822 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D822 |
| Film Tensile Strength at Break, TD | 57.9 MPa | 8400 psi | ASTM D822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 133 °C | 271 °F | DSC |
| Crystallization Temperature | 133 °C | 271 °F | Melting; DSC |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | |
| Blow-up Ratio (BUR) | 3.0 - 5.0 | 3.0 - 5.0 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LBF50-PA66 50% Long Basalt Fiber
- S&E Specialty Polymers GTP09005 PVC
- MarkeTech W90Cu Tungsten/Copper Heat Sink Material
- Solvay TECHNYL® C 218 V40 PA6, 40% glass fiber, Eh 50
- SPS Guang Zhou PONYLâ„¢ 4002G25 Flame Retardance/GF25%-PA66
- Sibur MPP 21015-E10 Frost Resistant Polypropylene
- Trimay® Wear Plate T161 Iron-based Steel Overlay
- Braskem LF320 LLDPE Cast Film Extrusion Polyethylene Copolymer
- Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Conditioned, 30% Glass Filled
- Total XSene® HD55110 High Density Polyethylene - Blown Film
Copyright © lookpolymers.com All Rights Reserved