- BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Conditioned)
BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1403-2 NF3001 is a 13% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | dry; ISO 1183 |
| Water Absorption | 7.4 % | 7.4 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 13 % | 13 % | 5mm/min; ISO 527 |
| Tensile Modulus | 3.90 GPa | 566 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Johnson Matthey Mattibraze 45 Cadmium Containing Silver Brazing Alloy
- Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours
- JPJ Technologies DG-1000 PVC
- SSAB Tunnplat Dogal F40 Metal-coated Mild Steel
- Techmer ES Plastiblend® PSU CR X
- A. Schulman POLYBATCH™ Red 5363 Concentrate Based In Polyethylene
- ExxonMobil Escorene™ UL 00018 Ethylene Vinyl Acetate Copolymer (European Grade)
- ExxonMobil 75W-80 Mobilfluid LT
- DuPont Performance Polymers Zytel® FN714 NC010A Nylon 66
- Arkema Group Pebax® MV 1074 SA 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved