Ravago Manufacturing Americas Hybrid B2035I Polycarbonate + PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hybrid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hybrid B2035I Polycarbonate + PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in North America High Impact Resistance Form: PelletsInformation provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 34 g/10 min @Load 3.80 kg, Temperature 260 °C |
34 g/10 min @Load 8.38 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
4.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.7 °C | 197 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nanosonic Metal Rubber™
- Premix Premi-Glas® 2103-25 CRSX Polyester BMC
- ExxonMobil Escorene® LD-133 LDPE Packaging Film Resin (discontinued **)
- Sharadaa Ceramics REFCAST C High Alumina Castables
- SK Chemicals SKYPET® BL8450 Specially Formulated PET Copolymer Resin
- Wellman Wellamid® MRGF25/15 42H-BKDX9 Nylon 6, 25% Mineral and 15% Glass Fiber Reinforced
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Mistron Vapor Filler
- Dynasol Calprene® H6171 Hydrogenated Rubber (SEBS)
- BASF Ultradur® B 4300 G6 FC 30% Glass Filled PBT
- Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
Copyright © lookpolymers.com All Rights Reserved