Category | Polymer , Thermoplastic , Nylon , Nylon 6-3 , Nylon 63, 35% Glass-Filled , Nylon 66 |
Manufacturer | |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | DSM Akulon® S223-HG6U (Dry) 33% Glass Reinforced Nylon 66 (North America)
(discontinued **).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
Water Absorption | 8.0 % | 8.0 % | Sim. to ISO 62 |
Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | Humidity Absorption; Sim. to ISO 62 |
Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-1/-2 |
Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527-1/-2 |
Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75-1/-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75-1/-2 |
Flammability, UL94 | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
IEC 60695-11-10 |
HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
IEC 60250 |
3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
IEC 60250 |
0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
IEC 60250 |
Descriptive Properties | Value | Comments |
---|---|---|
Heat stabilized or stable to heat | Yes | |
Injection molding | Yes | |
Lubricants | Yes | |
Release Agent | Yes | |
With Fillers | Yes |