Polymer Resources PPX-FRG30 Modified PPO, UL 94 V-1, 30% Glass Reinforced  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FRG30 Modified PPO, UL 94 V-1, 30% Glass Reinforced  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ASTM D955
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
Tensile Strength, Yield 110 MPa
16000 psi
ASTM D638
Flexural Strength 131 MPa
19000 psi
ASTM D790
Flexural Modulus 7.24 GPa
1050 ksi
ASTM D790
Izod Impact, Notched 0.961 J/cm
1.80 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
ASTM D648
Flammability, UL94 V-1
V-1
1/16 in
V-1
V-1
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 299 °C
480 - 570 °F
Middle Barrel Temperature 260 - 304 °C
500 - 580 °F
Front Barrel Temperature 271 - 310 °C
520 - 590 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 71.1 - 98.9 °C
160 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour