DSM Akulon® K224-G8 PA6-GF40

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® K224-G8 PA6-GF40.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% Glass Reinforced
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
dry; ISO 1183
Water Absorption 5.5 %
5.5 %
Sim. To ISO 62
Moisture Absorption 1.70 %
1.70 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0034 cm/cm
0.0034 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0083 cm/cm
0.0083 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 140 MPa
20300 psi
cond; ISO 527-1/-2
205 MPa
29700 psi
dry; ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
dry; ISO 527-1/-2
6.0 %
6.0 %
cond; ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
cond; ISO 527-1/-2
13.0 GPa
1890 ksi
dry; ISO 527-1/-2
Flexural Strength 275 MPa
39900 psi
dry; ISO 178
Flexural Modulus 10.8 GPa
1570 ksi
dry; ISO 178
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
8.50 J/cm²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
2.60 J/cm²

@Temperature 23.0 °C
12.4 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C
27.8 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
dry; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
dry; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
dry; IEC 60695-11-10
HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
dry; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
cond; IEC 60093
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
dry; IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
cond; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
dry; IEC 60250
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
dry; IEC 60250
4.4

@Frequency 1.00e+6 Hz
4.4

@Frequency 1.00e+6 Hz
cond; IEC 60250
14

@Frequency 100 Hz
14

@Frequency 100 Hz
cond; IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
cond; IEC 60243-1
35.0 kV/mm
889 kV/in
dry; IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
dry; IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
dry; IEC 60250
0.12

@Frequency 1.00e+6 Hz
0.12

@Frequency 1.00e+6 Hz
cond; IEC 60250
0.30

@Frequency 100 Hz
0.30

@Frequency 100 Hz
cond; IEC 60250
Comparative Tracking Index 500 V
500 V
cond; IEC 60112