SABIC Innovative Plastics LNP Thermocomp SF006S PA 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp SF006S PA 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D 792 |
| 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0021 - 0.0030 cm/cm @Time 86400 sec |
0.0021 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Time 86400 sec |
0.0070 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0074 - 0.0081 cm/cm @Time 86400 sec |
0.0074 - 0.0081 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D 638 |
| 108 MPa | 15700 psi | ISO 527 | |
| Elongation at Break | 4.6 % | 4.6 % | ISO 527 |
| 4.7 % | 4.7 % | ASTM D 638 | |
| Tensile Modulus | 6.55 GPa | 950 ksi | 50 mm/min; ASTM D 638 |
| 6.58 GPa | 954 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D 790 |
| 169 MPa | 24500 psi | ISO 178 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D 790 |
| 6.24 GPa | 905 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm @Temperature 23.0 °C |
2.79 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 9.61 J/cm @Temperature 23.0 °C |
18.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² @Temperature 23.0 °C |
27.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 43.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 113 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 113 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Covestro Texin® 5286 Thermoplastic Polyurethane, Polyether-based, Medical (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8167 PEEK, with carbon fiber, lubricant modified
- SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA 12 (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Mistron Vapor Filler
- DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17)
- Entec Hypel® PEHD18/.956 HDPE
- Covestro Makrolon® ET2613 Polycarbonate
- BASF Pluracol® 1538 Slabstock Foam Polyol
Copyright © lookpolymers.com All Rights Reserved