- DSM Akulon® CO-KGV4 /A JN.00.86 PA6-GF20 FR
DSM Akulon® CO-KGV4 /A JN.00.86 PA6-GF20 FR
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® CO-KGV4 /A JN.00.86 PA6-GF20 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
% Glass Reinforced, Heat Stabilized, Flame Retardant (halogen-phosphorous-free)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.5 % | 6.5 % | Sim. To ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 63.0 MPa | 9140 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| Tensile Modulus | 4.80 GPa | 696 ksi | dry; ISO 527-1/-2 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
dry; IEC 60695-11-10 |
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
dry; IEC 60695-11-10 | |
| Glow Wire Test | 725 °C @Thickness 1.60 mm |
1340 °F @Thickness 0.0630 in |
Glow Wire Ignition Temperature, dry; IEC 60695-2-13 |
| 725 °C @Thickness 0.800 mm |
1340 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature, dry; IEC 60695-2-13 | |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
dry; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.21 @Frequency 1.00e+6 Hz |
0.21 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
cond; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR2A-D-[color]-3 Polycarbonate, Flame Retardant, Medium Flow, UV-stabilized
- Reltek BONDiT™ C-52 Bonding Agent, Adhesive and Primer
- Overview of materials for Nylon 12, 20% Glass Fiber Filled
- Gouda Vuurvast VIBRON 160 H SiC Dense Vibrating Refractory Castable
- GRECO ISOPAK 525 ABS Resin
- Lanxess Durethan® TP 140-009 901510 Nylon 6, 15% Glass Fiber
- Hexcel® HexPly® F650 Bismaleimide Resin
- Arlon 55276R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved