Covestro Makrolon® AL 2647 Polycarbonate, Automotive Lens Injection Grade

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Optical Grade
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® AL 2647 Polycarbonate, Automotive Lens Injection Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Easy flowing injection molding grade, UV-stabilized, easy mold release agent.Applications: Automotive lens applications, fulfills U.S. specification SAE J 576C.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³
Water Absorption	0.35 %	0.35 %	Saturation in water
Moisture Absorption at Equilibrium	0.15 %	0.15 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.35 %	0.35 %
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955
Melt Flow	11 g/10 min @Load 1.20 kg, Temperature 300 °C	11 g/10 min @Load 2.65 lb, Temperature 572 °F

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	75	75	ASTM D785
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Tensile Strength, Yield	63.0 MPa	9140 psi
Elongation at Break	110 %	110 %	ASTM D638
Elongation at Yield	6.0 %	6.0 %
Tensile Modulus	2.40 GPa	348 ksi
Flexural Yield Strength	86.0 MPa	12500 psi	at 5% strain; ASTM D790
Flexural Modulus	2.30 GPa	334 ksi	ASTM D790
Izod Impact, Notched	8.00 J/cm @Thickness 3.20 mm	15.0 ft-lb/in @Thickness 0.126 in	ASTM D256
Charpy Impact Unnotched	NB	NB

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
Specific Heat Capacity	1.17 J/g-°C	0.280 BTU/lb-°F	ASTM D2766
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	136 °C	277 °F
Deflection Temperature at 1.8 MPa (264 psi)	129 °C	264 °F
Vicat Softening Point	143 °C	289 °F
Glass Transition Temp, Tg	148 °C	298 °F
UL RTI, Electrical	125 °C	257 °F
UL RTI, Mechanical with Impact	115 °C	239 °F
UL RTI, Mechanical without Impact	125 °C	257 °F
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
Oxygen Index	26 %	26 %

Optical Properties	Metric	English	Comments
Refractive Index	1.586	1.586
Haze	1.0 % @Thickness 3.20 mm	1.0 % @Thickness 0.126 in	ASTM D1003
Transmission, Visible	89 % @Thickness 1.00 mm	89 % @Thickness 0.0394 in	ISO 489-A

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm
Dielectric Constant	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz
	0.010 @Frequency 1e+6 Hz	0.010 @Frequency 1e+6 Hz
Comparative Tracking Index	275 V	275 V

Processing Properties	Metric	English	Comments
Melt Temperature	290 - 305 °C	554 - 581 °F