Toyobo GLAMIDE® T-402FR Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-402FR Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-402FR is a flame resistant, aromatic Nylon-6. It is of halogen origin and contains 30% GF.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 1.1 % | 1.1 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm @Thickness 1.00 mm |
0.0040 - 0.0080 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.010 - 0.013 cm/cm @Thickness 3.00 mm |
0.010 - 0.013 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 20 g/10 min | 20 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D638 |
| 92.0 MPa @Temperature 80.0 °C |
13300 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 215 MPa @Temperature -40.0 °C |
31200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.5 % | 3.5 % | Absolute Drying; ASTM-D638 |
| 4.6 % | 4.6 % | Practical Use (Water Absorption 1.9%); ASTM-D638 | |
| Flexural Strength | 95.0 MPa @Temperature 23.0 °C |
13800 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 |
| 125 MPa @Temperature 80.0 °C |
18100 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 200 MPa @Temperature 23.0 °C |
29000 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 235 MPa @Temperature -40.0 °C |
34100 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 5.40 GPa @Temperature 80.0 °C |
783 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 |
| 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D790 | |
| 9.80 GPa @Temperature 23.0 °C |
1420 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 12.5 GPa @Temperature -40.0 °C |
1810 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 140 MPa | 20300 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.800 J/cm @Temperature -40.0 °C |
1.50 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.9%); ASTM-D256 | |
| 1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.30 J/cm @Temperature 23.0 °C |
2.44 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.9%); ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 25 | 25 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 1.9%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 2.00 mm |
381 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.9%); ASTM-D149 |
| 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 15 sec | 15 sec | Practical Use (Water Absorption 1.9%); ASTM-D495 |
| 25 sec | 25 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 325 V | 325 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 40.0 - 60.0 MPa | 5800 - 8700 psi |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID® 6 NG1 GF 30 HLS PA6 reinforced with glass fiber, UV stabilized, hydrolysis resistant
- Precision Polymer Engineering V75P Fluoroelastomer Compound
- Gromax BFG30-AH00B2 Nylon 6 30% Glass Filled (Dry)
- Teknor Apex Flexalloy® 3500-70 Polyvinyl Chloride Elastomer
- Techmer ES HiFill® ABS GF20 BK 20% Glass Filled
- A. Schulman FORMION™ FI 391 Ionomer
- ExxonMobil 103 Mobilgrease XHP Series
- Dow FLEXOMER™ DFDB-9042 NT Very Low Density Polyethylene (VLDPE) Resin
- Asahi Kasei Thermofil P-20TC-5103 20% Talc Reinforced, Lubricated, Heat Stabilized
- Multibase C6-550 Dow-Corning Class VI Elastomer
Copyright © lookpolymers.com All Rights Reserved