Chosun Refractories HSC-15G Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-15G Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.004905 GPa @Temperature 110 °C, Time 86400 sec |
0.7114 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.005886 GPa @Temperature 1350 °C, Time 10800 sec |
0.8537 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| Compressive Strength | 34.3 MPa @Temperature 1350 °C, Time 10800 sec |
4980 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| 39.2 MPa @Temperature 110 °C, Time 86400 sec |
5690 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | limited |
| Shrinkage | -0.200 % @Temperature 1350 °C, Time 10800 sec |
-0.200 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.100 % @Temperature 110 °C, Time 86400 sec |
-0.100 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 50 % | 50 % | |
| CaO | 2.0 % | 2.0 % | |
| SiO2 | 45 % | 45 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Spray | |
| Material Required for Estimating(kg/?) | 2,200 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1760 TPE, PP Overmold or Standalone use
- ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP LF005 PEEK (Asia Pacific)
- A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE
- ExxonMobil LLDPE LL 6301XR Molding Linear Low Density Polyethylene Resin (European Grade)
- Dow AFFINITY™ PL 1840G Polyolefin Plastomer (POP)
- Asahi Kasei Thermofil P-40TC-1156 40% Talc Reinforced, Heat Stabilized
- Kleerdex Kydex® 1900 Acrylic/PVC Thermoplastic Sheet (discontinued **)
- M. Holland Company LD400 LDPE (discontinued **)
- DSM Arnite® TV4 460 KL PBT/PET Blend-30% Glass Reinforced (European Grade)
Copyright © lookpolymers.com All Rights Reserved