LNP ULTEM® SMU5872 Polyetherimide, 25% PTFE Lubricant  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP ULTEM® SMU5872 Polyetherimide, 25% PTFE Lubricant  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Not stand-alone resin: Compounding/ concentrate for wear resistance. Will be commercialized as UF2500.Features: Lubricated, Good Wear ResistanceForms: PelletsInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.7 MPa
10300 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 7.6 %
7.6 %
Type I, 5 mm/min; ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
(102 mm Span) 3mm/min; ASTM D790
Flexural Modulus 2.29 GPa
332 ksi
(102 mm Span) 3mm/min; ASTM D790
Izod Impact, Notched 0.374 J/cm
0.701 ft-lb/in
ASTM D256
Falling Dart Impact 6.21 J
4.58 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 196 °C

@Thickness 6.35 mm
385 °F

@Thickness 0.250 in
Unannealed; ASTM D648