Cossa Polimeri ESTABLEND 6500 Polycarbonate ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTABLEND
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Cossa Polimeri ESTABLEND 6500 Polycarbonate ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polycarbonate and Acrylonitrile Butadiene Styrene blendHigh thermal resistance, high impact resistanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 20 g/10 min
<br>@Load 5.00 kg,<br> Temperature 260 °C
 20 g/10 min
<br>@Load 11.0 lb,<br> Temperature 500 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
ASTM D 638
Tensile Strength, Yield 59.0 MPa
8560 psi
ASTM D 638
Elongation at Break >= 50 %
>= 50 %
ASTM D 638
Flexural Modulus 2.30 GPa
334 ksi
ASTM D 790
Izod Impact, Notched 4.70 J/cm
<br>@Temperature 0.000 °C
 8.81 ft-lb/in
<br>@Temperature 32.0 °F
 ASTM D 638
5.00 J/cm
<br>@Temperature 23.0 °C
 9.37 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 125 °C
<br>@Load 5.00 kg
 257 °F
<br>@Load 11.0 lb
 50°C/hr; ASTM D 1525
135 °C
<br>@Load 0.999 kg
 275 °F
<br>@Load 2.20 lb
 50°C/hr; ASTM D 1525
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in
Glow Wire Test 750 °C
<br>@Thickness 2.00 mm
 1380 °F
<br>@Thickness 0.0787 in
 I.E.C. 695-2-1